Thermodynamics for liquid-flame combustion in "hot" systems of a thermite type

Stoichiometric mixture	Pressure, P,MPa	Adiabatic temperature, Tad, K	Volume of evolved gases, Vg, litre/kg	Relative gas fraction, (m_g/m_in)	Main components of gas phase	Main condensed products
CrO₃ + 2Al	0.1	3364.28	2120	0.39	Cr, Al₂O, CrO	Al₂O₃(L)
	1	3534.70	212	0.38	same	same
	10	4331.34	13.4	0.20	same	Al₂O₃(L)
	50	4699.96	1.8	0.14	same	same
CrO₃ + 3Al + 2B	0.1	2697.02	1500	0.36	Cr, Al₂O, B₂O₂	Al₂O₃(L), CrB₂, Cr
	1	3068.86	130	0.28	same	same
	10	3579.40	8.5	0.16	same	Al₂O₃(L), CrB₂
	50	4091.63	0.11	0.02	same	same
3CrO₃ + 6Al + 2C	0.1	2711.11	2050	0.39	Cr, Al₂O, CO	Al₂O₃(L), Cr(L)
	1	3079.27	196	0.32	same	same
	10	3439.15	18	0.25	same	Al₂O₃(L), Cr(L), C₃Cr₇(L)
	50	3923.77	3	0.19	same	same
MoO₃ + 2Al	0.1	3808.21	430	0.09	Al₂O, MoO, MoO₂	Al₂O₃(L), Mo(L)
	1	4358.76	15	0.03	same	same
	10	4578.29	0	0	-	same
	50	4579.01	0	0	-	same
MoO₃ + 2Al + B	0.1	3157.13	820	0.15	Al₂O, B₂O₂, BO	Al₂O₃(L), Mo₂B(L)
	1	3389.45	73	0.13	same	Al₂O₃(L), Mo₂B(L), MoB(L)
	10	3958.40	4	0.06	Al₂O, B₂O₂	Al₂O₃(L), Mo₂B(L), MoB(L)
	50	4439.45	0	0	-	Al₂O₃(L), MoB(L)
MoO₃ + 2Al + 2B	0.1	2602.20	1025	0.26	Al₂O, B₂O₂	Al₂O₃(L), Mo₂B₅(L), MoB(C)
	1	2982.98	75	0.16	same	Al₂O₃(L), Mo₂B₅(L), MoB(L)
	10	3472.73	4.5	0.09	same	same
	50	3803.10	0	0	-	Al₂O₃(L), MoB(L), B(L)
2MoO₃ + 4Al + C	0.1	3082.12	990	0.15	Al₂O, CO	Al₂O₃(L), Mo(L)
	1	3103.93	100	0.15	same	same
	10	3417.13	8	0.11	same	Al₂O₃(L), Mo(L), CMo₂(L)
	50	3904.21	1	0.06	same	same